Method for manufacturing electro ceramic components

ABSTRACT

An array apparatus has a micromachined SOI structure, such as a MEMS array, mounted directly on a class of insulative substrate, such as low temperature co-fired ceramic or a thermal-coefficient of expansion matched glass, in which is embedded electrostatic electrodes disposed in alignment with the individual MEMS elements, where the electrostatic electrodes are configured for substantial fanout. In a specific embodiment in order to compensate for differences in thermal-expansion characteristics between SOI and ceramic, a flexible mounting is effected by means of posts, bridges and/or mechanical elements which allow uneven expansion in x and y while maintaining z-axis stability. Methods according to the invention include fabrication steps wherein electrodes are fabricated to a post-fired ceramic substrate and coupled via traces through the ceramic substrate to driver modules.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application is a division patent application of U.S. application Ser. No. 09/919,038 filed Jul. 30, 2001, having the same inventors and the same title.

BACKGROUND OF THE INVENTION

This invention relates to electro-ceramic components such as MEMS arrays and methods for fabricating electro ceramic components with high density interconnects and that maintain relative internal alignment. Components constructed according to the invention are MEMS arrays or other micromachined elements.

Conventional MEMS array structures comprise Silicon on Insulator (SOI) array structures in which is fabricated an integrated electrode array. One of the problems encountered is lack of scalability due to connector fan out limitations. A solution is needed. One possible solution might be found in array structures in development of XROS, Inc. of Sunnyvale, Calif.

XROS, Inc., in WIPO Publication WO 00013210 published Mar. 9, 2000, has disclosed elements of a hybrid structure for a MEMS array in which an SOI mirror or micromachined structure without electrodes is bonded to an unspecified insulating substrate on which is provided electrostatic electrodes for actuation of the mirror structure. The disclosure is silent about scaling of devices or about other provisions affecting operation in a thermally-stressed environment.

It has been discovered that the thermal coefficient of expansion mismatch between different components of an electro ceramic structure causes the structure to fall out of alignment, compromising the structure and the uniformity of operation of electrostatic actuators.

What is needed is a micromachined structure that can be scaled and be reliably manufactured and reliably operate over a range of temperature conditions.

SUMMARY OF THE INVENTION

According to the invention, an array apparatus has a micromachined SOI structure, such as a MEMS array, mounted directly on a class of substrate, such as low temperature co-fired ceramic, in which is embedded electrostatic electrodes disposed in alignment with the individual MEMS elements, where the electrostatic electrodes are configured for substantial fanout and the mounting allows for disparate expansion without degradation of performance. In a specific embodiment in order to compensate for differences in thermal-expansion characteristics between SOI and ceramic, a flexible mounting is effected by means of posts, bridges and/or mechanical elements which allow uneven expansion in x and y while maintaining z-axis stability.

Methods according to the invention include fabrication steps wherein electrodes are fabricated to a post-fired ceramic substrate and coupled via traces through the ceramic substrate to driver modules.

The invention will be better understood by reference to the following detailed description in connection with the accompanying illustrations.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a first embodiment according to the invention.

FIG. 2 is a side cross-sectional view of a single array element according to the first embodiment according to the invention.

FIG. 3 is a side cross-sectional view of a single array element according to a second embodiment according to the invention showing an alternative attachment scheme.

FIG. 4 is a side cross-sectional view of a single array element according to a third embodiment according to the invention showing an alternative attachment scheme.

FIG. 5 is a side cross-sectional view of a single array element according to a fourth embodiment according to the invention showing an alternative attachment scheme.

FIG. 6 is a side cross-sectional view of a single array element according to a fifth embodiment according to the invention showing an alternative attachment scheme.

FIG. 7 is a side cross-sectional view of a single array element according to a sixth embodiment according to the invention showing an alternative attachment scheme.

FIG. 8 is a side cross-sectional view of a single array element according to a seventh embodiment according to the invention showing an alternative attachment scheme.

FIG. 9 is a side cross-sectional view of a single array element according to an eighth embodiment according to the invention showing an alternative attachment scheme.

FIG. 10 is a side cross-sectional view of a single array element according to a ninth embodiment according to the invention showing an alternative attachment scheme.

DESCRIPTION OF SPECIFIC EMBODIMENTS

Reference is made to FIG. 1 and FIG. 2 in which is shown a MEMS array module 10 according to the invention referred to generally as a MEMS Multichip Module. Its central feature is a silicon oxide wafer 12 into which is built MEMS-based mirrors 14-17. Preferably the wafer is a Silicon on Insulator structure mounted on a multilayer insulative structure 18-1 to 18-N. According to the invention, for each mirror there is an array of electrodes 26, 28, 30, 32 placed on the first insulative structure 18-1 with vias 20, 22 and traces 21, 23 through multiple layers 18-1 to 18-N to a control module 40. According to the invention, a clamping fastener 42 is placed at selected locations over the surface of the wafer 12. In addition, xy position locks 46, 48 are disposed at the boundaries of the wafer 12 to secure the wafer 12 to a frame 50. A mirror surface electrical connection 52 is coupled through vias 54, 56 to an external power source (not shown). Coupling to the connection 52 to the electrically conductive surface of the mirrors 14 is through four actuation elements 58, 60, 62, 64 around the perimeter of each mirror cavity. Components such as a resistor 66 may be buried in place along a trace for coupling electrodes to the control module 40 by direct attachments 68. A thermal control device 70, such as a heat sink or active thermal transfer element, is attached to the control module. An important feature of the invention is the provision of z clamping fasteners 42 which have various forms to restrain movement in the z-axis while permitting limited movement in the xy plane. To this end, pins 72, 74, 76, 78 are provided for each fastener 42 of the specific embodiment. The pins are held in place in the fastener by for example solder 80 which fill in shafts. The fastener 42 is a rigid, electrically conductive element. The pins 72, etc. each have a foot 82 that is bonded to the metallization 84. At the periphery of the wafer 12, an electrical contact to the bottom of the wafer is made through a mechanical connection 85. The wafer 12 comprises a conductive silicon layer 86, an insulative silicon oxide layer 88 and a conductive silicon structure 90, onto which is applied a metallized reflective surface 92, particularly in the mirror regions. According to the invention, the wafer 12 is not bonded to the underlying Low Temperature Cofired Ceramic (LTCC) layer 18, except at fastening points along the edges, so that the wafer 12 is able to expand and contract laterally but not vertically relative to the LTCC layer 18.

Reference is made to FIG. 3. In this embodiment a clamping fastener 142 is provided in which only a single pin 72 is employed. This structure is more space efficient.

Reference is made to FIG. 4 in which a monolithic bridge fastener 242 is provided. The bridge fastener 242 is attached to the insulative substrate through, for example solder or brazing.

Reference is made to FIG. 5 and FIG. 6 in which chip attach methods connect silicon 86 to the insulative substrate 18 within a cavity 190, making electrical contact to the bottom layer of the MEMS structure. Wire bond 192 makes an electrical connection to the top silicon surface. In FIG. 5, a solder ball 194 secured to upper and lower metallizations 196, 198 permits x and y movement and restrains vertical movement. Instead of a solder ball, a pair of gold stud bumps could be respectively bonded to the metallizations and fused to form a bond restraining z movement while allowing flexure in the xy plane.

In FIG. 6, a metal bump 296 is bonded to a metallization 294 on one side and to a conductive epoxy adhesive 298 on the other side to permit x and y movement and restrain vertical movement.

Reference is made to FIG. 7. The silicon wafer 86 is attached to the substrate 18 with a non-conductive but flexible adhesive 200. Wire bond 192 makes electrical connection to the top silicon surface. A compliant conductive material 202 makes electrical connection to the bottom layer of the silicon layer 86.

Reference is made to FIG. 8. Precision spacers 204, 206, 208 are employed and embedded in the non-conductive adhesive 200 to establish height. These can be beads or bars, for example.

Reference is made to FIG. 9. Similar to the embodiment of FIG. 7, herein an anisotropic conductive adhesive 302 is used instead of a non conductive adhesive, thus making the bottom layer an electrical connection.

Reference is made to FIG. 10. Similar to the embodiment of FIG. 4, but also applicable to embodiments of FIG. 2 and FIG. 3, a compliant conductive material 402 is placed as a washer or shim between the locking cap or bridge 242 and the wafer 12, wherever a cap or bridge is used.

In operation, electrodes 26, 28, 30, 32 placed directly on the substrate 18 actuate the mirrors 14 through electrostatic force. The present structure simplifies the fabrication and improves the fabrication yield of the mirror structures by eliminating the need for the electrodes to be included as part of the MEMS wafer 86 substrate. Because of this, larger mirror arrays become feasible.

Mounting the wafer or MEMS structure directly onto the mechanically robust LTCC layer or other printed circuit laminate (PCL) material (the “substrate”) 18 reduces the stresses placed upon large MEMS structures. By using fasteners to clamp the MEMS structure to the substrate means that near zero height is added to the module and eliminate the possibility of delamination caused by thermal mismatch. Filling the gap between the edge of the MEMS structure and the substrate with a compliant material locks position of mirrors over electrodes. This method eliminates the need to rely on the shear strength of this material.

The invention has a number of structural advantages that permit scaling.

Direct chip attachment of the drive circuitry to the back of the substrate permits high density circuit fabrication. The substrate itself facilitates interconnection. This structure has resistors buried in the multilayer ceramic and thus the resistors are not inconveniently large and discrete.

Fabrication can take advantage of post-fire metallization and dielectric placement on ceramic, thus overcoming shrinkage issues associated with firing. The structures are also robust as compared to other structures. A variety of attachment combinations can now be employed:

Silicon to Ceramic board materials;

Silicon to Fiber/Ceramic matrix board materials;

Silicon to Polyimide materials;

Silicon to Flex circuit board materials;

Silicon wafer to Silicon substrate;

Silicon to Thick film on any substrate material;

Silicon to Thin film on any substrate material.

The invention has been explained with reference to specific embodiments. Other embodiments will be evident to those of ordinary skill in the art. Therefore, it is not intended that this invention be limited, except as indicated by the appended claims. 

What is claimed is:
 1. A method for fabricating a micromachined apparatus comprising the steps of: providing a wafer with a metallized obverse surface; etching an array of a cavity and hinges in said wafer thus forming an array of a conductive handle and a mirror with metallization on an obverse surface; releasing oxide holding the mirror; metallizing walls of the cavity and a reverse surface of said mirror; providing a ceramic structure of stacked metallization and insulative ceramic layers; providing first and second electrodes on an obverse surface of said ceramic structure, said electrodes being disposed to confront said mirror; electrically connecting the electrodes to a driver on a reverse side of the ceramic structure via traces through said ceramic structure; providing at least one bonding element extending from the obverse side of the ceramic structure; juxtaposing said wafer and said ceramic structure, said at least one mounting pin extending through an alignment hole in said wafer, said alignment hole having lateral spacing to permit relative motion in x and y; and providing a constraint on said bonding element to constrain relative motion of said ceramic and said wafer along a z-axis.
 2. The method according to claim 1 wherein said constraint is a cap.
 3. The method according to claim 1 further including: providing centering means to bias x and y motion to a neutral position.
 4. The method according to claim 1 wherein said relative motion is constrained by a self-centering biasing means.
 5. The method according to claim 2 wherein said bonding element is a first alignment pin, further including the step of: providing at least a second alignment pin; and providing a bridge between said first alignment pin and second alignment pin, said bridge being slidably juxtaposed to said SOI wafer to constrain motion in the z axis.
 6. The method according to claim 5 further including the step of: providing at least a third alignment pin; and providing a stabilizing bridge between said first alignment pin, said second alignment pin and said third alignment pin.
 7. The method according to claim 1 further including: firing said ceramic structure; and mounting said electrodes to said ceramic structure after firing said ceramic structure. 